| hysical | Nominal Value | Unit | Test Method |
| 1.21 | g/cm3 | ASTM D792 |
Specific Volume | 0.830 | cm3/g | ASTM D792 |
| 1.22 | g/cm3 | ISO 1183 |
| 16 | g/10 min | ISO 1133 |
| 15.0 | cm3/10min | ISO 1133 |
| 0.80 to 1.0 | % | Internal Method |
| 0.80 to 1.0 | % | Internal Method |
| 0.50 | % | ISO 62 |
| 0.15 | % | ISO 62 |
| f2 | | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
| | | ASTM D638 |
-- 3 | 2250 | MPa | |
-- 4 | 2250 | MPa | |
| 2050 | MPa | ISO 527-2/1 |
| 53.0 | MPa | ASTM D638 |
| 50.0 | MPa | ISO 527-2/50 |
| 51.0 | MPa | ASTM D638 |
| 50.0 | MPa | ISO 527-2/50 |
| 4.0 | % | ASTM D638 |
| 4.0 | % | ISO 527-2/50 |
| 120 | % | ASTM D638 |
| 120 | % | ISO 527-2/50 |
| 2030 | MPa | ASTM D790 |
| 2000 | MPa | ISO 178 |
| 80.0 | MPa | ISO 178 |
| 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
| 55 | kJ/m2 | ISO 179/1eA |
| | | ASTM D256 |
-40°C | 300 | J/m | |
-30°C | 530 | J/m | |
23°C | 710 | J/m | |
| | | ISO 180/1A |
-30°C | 30 | kJ/m2 | |
23°C | 50 | kJ/m2 | |
| 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
| 107 | °C | ASTM D648 |
| | | ASTM D648 |
1.8 MPa, Unannealed, 3.20 mm | 84.0 | °C | |
1.8 MPa, Unannealed, 6.40 mm | 99.0 | °C | |
| 75.0 | °C | ISO 75-2/Af |
| 122 | °C | ASTM D1525 12 |
| | | |
-- | 120 | °C | ISO 306/B50 |
-- | 125 | °C | ISO 306/B120 |
CLTE - Flow (-40 to 40°C) | 9.5E-5 | cm/cm/°C | ASTM E831 |
CLTE - Flow (-40 to 40°C) | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse (-40 to 40°C) | 9.0E-5 | cm/cm/°C | ASTM E831 |
CLTE - Transverse (-40 to 40°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| 75.0 | °C | UL 746 |
| 75.0 | °C | UL 746 |
| 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
| PLC 5 | | ASTM D495 |
| PLC 1 | | UL 746 |
| PLC 0 | | UL 746 |
| PLC 0 | | UL 746 |
| PLC 3 | | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
| HB | | UL 94 |